Sign In | Join Free | My china-telecommunications.com
China Bicheng Electronics Technology Co., Ltd logo
Bicheng Electronics Technology Co., Ltd
We Are Your RF PCB Solution Provider! Rogers PCB, Taconic PCB, Arlon PCB, F4B PCB ISO9001, ISO14001, IATF 16949 certified
Verified Supplier

5 Years
Home > FR4 PCB Board >

Lead Free Multilayer Printed Circuit Board E glass coated

Product Categories
Bicheng Electronics Technology Co., Ltd
Trust Seal
Verified Supplier
Credit Check
Supplier Assessment
Contact Now

Lead Free Multilayer Printed Circuit Board E glass coated

Brand Name : Bicheng

Model Number : BIC-502.V1.0

Certification : UL, ISO9001, IATF16949

Place of Origin : CHINA

MOQ : 1PCS

Payment Terms : T/T

Supply Ability : 5000PCS per month

Delivery Time : 8-9 working days

Packaging Details : Vacuum bags+Cartons

Base material : High-Tg and High Thermal Reliability Epoxy Resin

Layer count : Double Layer, Multilayer, Hybrid PCB

PCB thickness : 10mil (0.254mm), 15mil (0.381mm), 20mil (0.508mm), 25mil(0.635mm), 30mil (0.762mm), 62mil(1.575mm)

PCB size : ≤400mm X 500mm

Solder mask : Green, Black, Matt Black, Blue, Matt Blue, Yellow, Red etc.

Copper weight : 0.5oz (17 µm), 1oz (35µm), 2oz (70µm), 3oz (105µm), 4oz (140µm), 5oz (175µm)

Surface finish : Bare copper, HASL, ENIG, OSP, Immersion tin, Immersion Silver etc..

Contact Now

High Tg Lead Free Multi-layer Printed Circuit Board Built on TU-768 Core and TU-768P Prepreg

(Printed Circuit Boards are custom-made products, the picture and parameters shown are just for reference)

General Description

TU-768 / TU-768P laminate / prepreg are made of high quality woven E-glass coated with the epoxy resin system, which provides the laminates with UV-block characteristic, and compatibility with automated optical inspection (AOI) process. These products are suitable for boards that need to survive severe thermal cycles, or to experience excessive assembly work. TU-768 laminates exhibit excellent CTE, superior chemical resistance and thermal stability plus CAF resistance property.

Lead Free Multilayer Printed Circuit Board E glass coated

Main Applications

Consumer Electronics

Server, workstation

Automotive

Key Features

Lead Free process compatible

Excellent coefficient of thermal expansion

Anti-CAF property

Superior chemical and thermal resistance

Fluorescence for AOI

Moisture resistance

Our PCB Capability (TU-768)

High Tg Lead Free Multi-layer Printed Circuit Board Built on TU-768 Core and TU-768P Prepreg High-Tg and High Thermal Reliability Epoxy Resin
Designation: TU-768
Dielectric constant: 4.3
Layer count: Double Layer, Multilayer, Hybrid PCB
Copper weight: 0.5oz (17 µm), 1oz (35µm), 2oz (70µm), 3oz (105µm), 4oz (140µm), 5oz (175µm)
PCB thickness: 10mil (0.254mm), 15mil (0.381mm), 20mil (0.508mm), 25mil(0.635mm), 30mil (0.762mm), 62mil(1.575mm)
PCB size: ≤400mm X 500mm
Solder mask: Green, Black, Matt Black, Blue, Matt Blue, Yellow, Red etc.
Surface finish: Bare copper, HASL, ENIG, OSP, Immersion tin, Immersion Silver etc..
Technology: HDI, Via in pad, Impedance Control, Blind via/Buried via, Edge Plating, BGA, Countsunk Holes etc.

Lead Free Multilayer Printed Circuit Board E glass coated

Typical Properties of TU-768

Typical Values Conditioning IPC-4101 /126
Thermal
Tg (DMA) 190°C
Tg (DSC) 180°C > 170°C
Tg (TMA) 170°C E-2/105
Td (TGA) 350°C > 340°C
CTE x-axis 11~15 ppm/°C N/A
CTE y-axis 11~15 ppm/°C E-2/105 N/A
CTE z-axis 2.70% < 3.0%
Thermal Stress,Solder Float, 288°C > 60 sec A > 10 sec
T260 > 60 min > 30 min
T288 > 20 min E-2/105 > 15 min
T300 > 2 min > 2 min
Flammability 94V-0 E-24/125 94V-0
DK & DF
Permittivity (RC 50%) @10GHz 4.3
Loss Tangent (RC 50%) @10GHz 0.018
Electrical
Permittivity (RC50%)
1GHz (SPC method/4291B) 4.4 / 4.3 < 5.2
5GHz (SPC method) 4.3 E-2/105 N/A
10GHz (SPC method) 4.3 N/A
Loss Tangent (RC50%)
1GHz (SPC method/4291B) 0.019 /0.018 < 0.035
5GHz (SPC method) 0.021 E-2/105 N/A
10GHz (SPC method) 0.023 N/A
Volume Resistivity > 1010 MΩ•cm C-96/35/90 > 106 MΩ•cm
Surface Resistivity > 108 MΩ C-96/35/90 > 104 MΩ
Electric Strength > 40 KV/mm A > 30 KV/mm
Dielectric Breakdown > 50 kV A > 40 KV
Mechanical
Young’s Modulus
Warp Direction 25 GPa A N/A
Fill Direction 22 GPa
Flexural Strength
Lengthwise > 60,000 psi A > 60,000 psi
Crosswise > 50,000 psi A > 50,000 psi
Peel Strength, 1.0 oz RTF Cu foil 7~9 lb/in A > 4 lb/in
Water Absorption 0.18% E-1/105+D-24/23 < 0.8 %


Product Tags:

Lead Free Multilayer Printed Circuit Board

      

E Glass Coated Printed Circuit Board

      

Hybrid PCB Printed Circuit Board

      
Quality Lead Free Multilayer Printed Circuit Board E glass coated for sale

Lead Free Multilayer Printed Circuit Board E glass coated Images

Inquiry Cart 0
Send your message to this supplier
 
*From:
*To: Bicheng Electronics Technology Co., Ltd
*Subject:
*Message:
Characters Remaining: (0/3000)
 
You May Like